JET FIRE HOSE LATEX
LATEX were the original hoses in the JET HOSE range and they have made a major contribution to the success of Ashimori.
LATEX hoses feature a strong, thin, durable latex lining applied to a woven jacket
with ToughEdge. They are lighter, more compact and easier to handle than other
rubber lined fire hoses, features which have made them popular around the world. |
★Features
1. |
Most lightweight
and compact of all rubber lined hoses. |
2. |
ToughEdge
jacket resists abrasion,cuts and nicks. |
3. |
Easy handling. |
4. |
High water
dischage efficiency thanks to reduced friction loss.
ensure durability. |
| Size |
product |
LATEX ACE |
LATEX DIA |
LATEX STAR |
A-0NE |
| Working Pressure |
229p.s.i.
(16kg/cm2) |
186p.s.i.
(13kg/cm2) |
186p.s.i.
(13kg/cm2) |
143p.s.i.
(10kg/cm2) |
| Test Pressure |
500p.s.i.
(35kq/cm2) |
450p.s.i.
(31kg/cm2) |
400p.s.i.
(28kg/cm2) |
300p.s､i.
(21kg/cm2) |
2 1/2″
(65mm) |
Weight/20m |
16.0lbs(7.2kg) |
13.9lbs(6.3kg) |
13.4lbs(6.1kg) |
13.4lbs(6.1kg) |
| Coiling Dia. |
18.1″(46cm) |
16.1″(41cm) |
15.4″(39cm) |
15.4″(39cm) |
| Burstiing Pressure |
814p.s.i.
(57kg/cm2) |
686p.s.i.
(48kg/cm2) |
600p.s.i.
(42kg/cm2) |
600p.s.i.
(42kg/cm2) |
2″
(50mm) |
Weight/20m |
15.1lbs(6.8kg) |
9.7lbs(4.4kg) |
- |
- |
| Coiling Dia. |
17.3″(44cm) |
16.1″(41cm) |
- |
- |
| Burstiing Pressure |
857p.s.i.(60kg/cm2) |
729p.s.i.(5.1kg/cm2) |
- |
- |
1 1/2″
(40mm) |
Weight/20m |
11.5lbs(5.2kg) |
8.4lbs(3.8kg) |
8.4lbs(3.8kg) |
8.4lbs(3.8kg) |
| Coiling Dia. |
15.4″(39cm) |
15.4″(39cm) |
14.6″(37cm) |
14.6″(37cm) |
| Burstiing Pressure |
857p.s.i.
(60kg/cm2) |
814p.s.i.
(57kg/cm2) |
814p.s.i.
(57kg/cm2) |
471p.s.i.
(33kg/cm2) |
| For inquiries regarding our products: |
|
Safety & Fire Protection
Equipment Sales Dept. |
(Head Office) |
| (Tokyo Office) |
|
|
TEL
TEL |
|
06-6533-9258
03-3246-7302 |
|
FAX
FAX |
|
06-6533-9290
03-3246-7310 |
|
|
| For inquiries via email: |
|
Safety & Fire Protection
Equipment Sales Dept. (Head Office) |
|
|
|
|